[[File:Shl.jpg|缩略图|300px|[https://image.baidu.com/search/detail?ct=503316480&z=0&ipn=d&word=金属深冷处理&step_word=&hs=0&pn=12&spn=0&di=75350&pi=0&rn=1&tn=baiduimagedetail&is=0%2C0&istype=2&ie=utf-8&oe=utf-8&in=&cl=2&lm=-1&st=-1&cs=3140940434%2C1073160686&os=2776801947%2C1460838433&simid=3422009368%2C488000945&adpicid=0&lpn=0&ln=724&fr=&fmq=1582364865034_R&fm=result&ic=&s=undefined&hd=&latest=&copyright=&se=&sme=&tab=0&width=&height=&face=undefined&ist=&jit=&cg=&bdtype=0&oriquery=&objurl=http%3A%2F%2Ffile03.zk71.com%2FFile%2FCorpProductImages%2F2011%2F08%2F10%2F0_xahmdlyzp179_20110810113244.jpg&fromurl=ippr_z2C%24qAzdH3FAzdH3Fooo_z%26e3Bzh08_z%26e3Bv54AzdH3Fr6517vpfAzdH3F79mbadbAzdH3Fxwi41syzr80l_n0n9b9m8_z%26e3Bip4s&gsm=d&rpstart=0&rpnum=0&islist=&querylist=&force=undefined 原圖鏈接][http://www.zk71.com/products/u468028/xahmdlyzp179_37348461.html 来自西安恒茂动力科技有限公司]深冷处理设备]]
'''冷处理''' 所谓冷处理就是将[[淬火]]钢深冷至室温以下的处理方法。

钢件淬火后，再迅速将其冷却到室温以下的某一温度，使淬火后的残余[[奥氏体]]转变为[[马氏体]]，以增加钢件硬度和尺寸稳定性的[[热处理工艺]]。冷处理实际上是淬火过程的继续。也有称做低温处理（或[[深冷处理]]）的。

就冷处理的温度而言，即使在-190℃进行处理仍有一定（一般为百分之几）残存的奥氏体被保留下来。因此，一般用-100～-80℃就足够了。冷处理时间一般有30～90min就足够了。

冷处理可有效防止置裂。当钢件急冷到常温并在常温下放置时，其残存的奥氏体将缓慢向马氏体转化，由于这种转变会导致内应力增加，最后就会开裂。<ref>[https://www.sohu.com/a/257993518_821100 解开神秘材料处理工艺的面纱---深冷处理 ],搜狐，2018-10-07 </ref>