{| class="https://image.baidu.com/search/index?ct=201326592&tn=baiduimage&word=%E6%B0%A7%E5%8C%96%E7%9A%AE&pn=6&spn=0&ie=utf-8&oe=utf-8&cl=2&lm=-1&fr=&se=&sme=&cs=1870539701%2C3060246714&os=3717834899%2C128761670&objurl=https%3A%2F%2Fgimg2.baidu.com%2Fimage_search%2Fsrc%3Dhttp%3A%2F%2Fbkimg.cdn.bcebos.com%2Fpic%2Fcc11728b4710b9125f53ecdac1fdfc0392452207%26refer%3Dhttp%3A%2F%2Fbkimg.cdn.bcebos.com%26app%3D2002%26size%3Df9999%2C10000%26q%3Da80%26n%3D0%26g%3D0n%26fmt%3Dauto%3Fsec%3D1672164287%26t%3Ddbf82d971cfb2c8afb34587677c651ce&di=7163459808492781569&tt=1&is=0%2C0&adpicid=0&gsm=3c" style="float:right; margin: -10px 0px 10px 20px; text-align:left"
|<center>'''氧化皮'''<br><img
src="https://gimg2.baidu.com/image_search/src=http%3A%2F%2Fbkimg.cdn.bcebos.com%2Fpic%2Fcc11728b4710b9125f53ecdac1fdfc0392452207&refer=http%3A%2F%2Fbkimg.cdn.bcebos.com&app=2002&size=f9999,10000&q=a80&n=0&g=0n&fmt=auto?sec=1672164287&t=dbf82d971cfb2c8afb34587677c651ce " width="280"></center><small>  圖片來自百度</small> 
|}
氧化皮是钢铁在高温下发生[[氧化作用]]而形成的腐蚀产物，由[[氧化亚铁]]、[[四氧化三铁]]、[[三氧化二铁]]组成。从内向外为：氧化亚铁、四氧化三铁、三氧化二铁。其中氧化亚铁结构疏松，保护作用较弱，而四氧化三铁、三氧化二铁结构致密，有较好的保护性。一般减少金属氧化 的措施是：(1)料温在1000℃以下时，可 采用氧化性炉气，以便形成的氧化皮易于清除，而此时温度不高，氧化尚不激烈；(2) 料温在1000℃以上时，采用还原性炉气，这时应减少进入炉内的空气量， 以免氧化皮产生过多。此外，采用快速加 热、缩短加热时间和少氧化、无氧化加热方 法，都是积极减少金属氧化的措施。

钢在加热时，铁与氧或铁与燃料燃烧时 的生成物 （CO2、H2O汽等） 的化学作用， 而形成一层氧化层，称为氧化皮。在被加热坯料表面分布 成三层；最内层由细小颗粒的FeO组成，占 氧化层全厚的40%； 中间层由粗大颗粒的 Fe3O4组成，占其厚度的50%左右； 最外层 由Fe2O3组成，占10%左右。由于氧化铁 皮和钢的膨胀系数不一致，故疏松而易于脱 落，同时氧化铁皮的熔点 （1300～1350℃） 较低，致使钢在高温下加热时，氧化铁皮的 脱落或熔化会暴露出金属的表面，因而使氧 化继续不断地加速进行。